Improving CASS TEST RATING of hard chrome

adv.   auto technology banner

(2001)

HOW TO GET CASS RATING OF 10 (NO CORROSION IN 96 HRS SPRAY).INFLUENCING FACTORS IN HARD CHROME 30 MICRONS PLATING.

C.JAYAKRISHNAN
- BANGALORE, INDIA


(2001)

Probably an underplate of nickel will do the most good.

pooky
tom pullizi signature
Tom Pullizzi
Falls Township, Pennsylvania

(2001)

Hard chrome plating is not usually tested by CASS but by NSST.

George Shahin
George Shahin
Atotech - Rock Hill, South Carolina



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView This Week's HOT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.