Could anyone kindly advise me if the electrophoresis coating is non-conductivity or not?
Thanks,
Jeff Ren- Dongguan City, China
2001
It's non-conductive. Actually, that's why it works. If it weren't non-conductive, the high current density areas would not get blocked off so there would be no current flow to the low current density areas and the treatment would be ineffective.

Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey