topic 9027

Hot dip galvanized vs. standard zinc plated in 95% humidity 60 degree constant temp.

(2001)

I am providing steel conduit and hardware to be installed in a freight tunnel system in Chicago. Several of our components are simply zinc plated. I need to provide some information on the lifecycle of Zinc plating in that tunnel environment, which is reported to be 95% humidity at 60 °F constant. Is there a corrosion resistance chart available that I could use for reference.

Steve Hickernell
communications - Wadsworth, Ohio, USA



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Comment to THIS thread START a NEW threadView CURRENT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2018 finishing.com, Inc., Pine Beach, NJ   -   About finishing.com   -  Privacy Policy
How Google uses data when you visit this site.