Whitish colour after electropolish on SS316L

We are doing welding SS316L then polish by very fine grid size abrasive material. Then we do electropolish. This time we saw some of the jobs are getting whitish finish. Why?

Chandu Bhojane
Engineer - Pune
November 29, 2010

It could be the part not clean (possibly a new grit source) or the temperature was not correct or the temp was stratified or the solution is out of spec or is contaminated.

James Watts
- Navarre, Florida
December 1, 2010

Sorry! Finishing.com is temporarily Read-Only.
Ted Mooney is retiring but I have several offers to take it over.
We're working hard to make sure we find it the best new home.

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: