Patina 500 sq. ft. copper clad elevator shaft




We have clad a three story elevator shaft with 20 oz. copper and would like to patina it. It was built in two stages so half has aged 1 year and the other half is shiny. Any ideas?

Barry VanRiper
Construction project manager - Washington, DC
September 3, 2009



Well, it depends on the patina you are looking for. If you wish to artificially age it then you can go with the standard Miracle Grow treatment, the fact that one part is older than the other shouldn't be a problem, it will all turn greenish.
Now if you are after a more advanced finish, beyond just oxidizing the finish you need to be more specific about what you want to do to it.

Marc Banks
Blacksmith - Boone, North Carolina
September 6, 2009




(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact  -  Privacy Policy  -  ©1995-2024 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"