Solderability of plated aluminium


(2000)

We are looking for a material with good solderibility and corrosion resistance that can be plated onto Aluminium. We understand that Nickel plating becomes passive over time, decreasing its solderibility. Does anyone know of any methods to slow down or stop this process, or alternative materials that would suit this application.

Mark Thompson
TRW - UK


(2000)

Without knowing what it is that you wish to plate, I can only suggest that aluminum busbar is often copper plated. Then it can be tin or silver plated, all over or just on the solderable surfaces. If aesthetics are not a concern, copper plating followed by immersion tinning or immersion silvering might be the best approach.

Ted Mooney, finishing.com Teds signature
Ted Mooney, P.E. RET
finishing.com
Pine Beach, New Jersey



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView CURRENT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.