Passivation to meet AMSQQP35 TYPE 2/ TYPE 8

Is there any other way to passivate stainless to meet with military QQ-P-35C [link is to free spec at Defense Logistics Agency, dla.mil] TYPE 2/ TYPE 8 without the use of Nitric Acid?

Dustin Colina
electropolishing - Clearwater, Florida
2005

adv.
We have developed passivation technology based on low concentration of phosphoric acid. It is environmentally friendly and can be applied for food industry also. Contact us for details.

Anna Berkovich
Russamer Lab

Pittsburgh, Pennsylvania

2005

Dustin, you can passivate without using nitric acid, as Anna says, and as other folks who use citric acid will tell you. Yet AMSQQP35 [canceled] Type 2 or Type 8 both require nitric acid. If you're locked into using that specification, you are locked into using nitric acid based formulations.

Lee Gearhart
metallurgist - E. Aurora, New York
2005

www.finishing.com is made possible by supporting advertisers ...
this text gets replaced with bannerText

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: