topic 3961

Problems in Powdercoating of Aluminum 6063


(1999)

Problem: Powder coating 6063 anodized alum (webster 4-7) 2" x 1/2" x 40' long rail. 18 stanchions attached 1 1/4 dia x 1 1/2 long.

1. Please explain to me the correct process. I understand powder coating steel but not alum.

2. Please explain to me the correct steps for recoating rejected parts.

John Bruhn
tool company - Syracuse, Indiana


February 28, 2009

Hi, John. The biggest difference is in the pretreatment. While steel is phosphated, aluminum should ideally be chromate conversion coated (sometimes called Alodine or Iridite because these are two major trade names for the process.

The process usually includes caustic cleaning, etching, and desmutting in addition to the chromate conversion coating step per se.

Regards,

Ted Mooney, finishing.com Teds signature
Ted Mooney, P.E. RET
finishing.com
Pine Beach, New Jersey



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView This Week's HOT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.