Trivalent Chromate Surface Conductivity




Can you tell me what the surface conductivity or the volumetric resistance is for Trivalent Chromate alone?

Gary Doerr
EMC Engineer - Sunnyvale, California
2005



2005

The answer to your question is that it would be variable from process to process. Then you would have variation in how the finish is applied and the process bath maintained.

What I am really getting at is the thickness of the chromate film will effect conductivity and different proprietary products will have different results. Further the application would include further variables,
not including the use of sealers, organic dyes, etc.

Gene Packman
process supplier - Great Neck, New York




(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact  -  Privacy Policy  -  ©1995-2024 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"