Nickel plating is peeling off from copper plating

2004

Hello.

I have plated decorative chrome plating on steel parts and have one problem to work through. The steel part came from a cyanide copper bath, following by the bright copper acid, Watts bright nickel and decorative chrome bath. My problem get in touch with peeling (poor adhesion) of the nickel coating over the copper coating. This fail just appear after the chrome plating. Moreover, just some parts (from the same rack)have this problem. Thanks very much for any help.

Best regards,

Jean Vicente
Chemist - São Paulo, São Paulo, Brazil

GM, while parts are immersed in Watts Nickel bath current should be "on" to over come the problem of adhesion.

Shankara Narayanan N
- Bangalore, Karnataka, India
2004

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: