Parts rusting in-process in humid atmosphere

We have done Indirect/Direct evaporative cooling for a Automobile components Manufacturing Facility and the RH of 65% and Dry bulb of 28 °C is maintained and the products are rusting within two shifts of eight hours/shift. How it can be minimised/prevented?

Sridhar Vijayaraghavan
contractor - Chennai, Tamilnadu, India
2003

Your question is a little vague, Sridhar, and it sounds rather impractical to make the parts more humidity resistant with a rust preventative or by changing their material. So it's hard to suggest anything beyond: "Reduce the humidity!". Good luck.

Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey
2003

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: