Oxalic vs sulfuric Anodizing of Aluminum

probertEthumb
Aluminum How-To
"Chromating - Anodizing - Hardcoating"

by Robert Probert

Also available in Spanish

You'll love this book. Finishing.com has sold almost a thousand copies without a single return request :-)


"The Surface
Treatment &
Finishing of
Aluminium and
Its Alloys"

by Wernick, Pinner
& Sheasby

pinner
on eBay
or Amazon
or AbeBooks

(affil link)

I need to know if there is a difference between Oxalic and Sulfuric anodization. I know that the colour will differ and I think there is an issue with pore sizes, but will this affect their function as a wear resistant hard coating where there are no temperature or pH considerations?

John Hayes
medical equipment supplier - Dublin City, County Dublin, Ireland
2003




(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread


Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

Finishing
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g,
& Software


About/Contact  -  Privacy Policy  -  ©1995-2025 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"