topic 2460

Nickel-plating stainless


(1998)

To All:

I would like to effectively barrel nickel-plate stainless(304) steel parts and would like some recommendations. Currently the parts are peeling and blistering in a few areas on the surface. I am not sure if the part is oxidizing prior to nickel plate or is passive(not receiving a good contact in nickel strike). We utilize nickel sulfamate chemistry and a woods nickel strike bath. The part is electro-polished prior to plate and also receives a cathodic clean, so the part should be clean. I wasn't sure if the process needed a stainless steel activate prior to nickel strike and what the chemistry would consist of. Any recommendations would be appreciated and thanks in advance.

Dave Bernardini



No. 1 of 2 simultaneous responses:

(1998)

My 2 cents worth is that it absolutely needs an acid etch/activate. Electropolish will make the surface very passive, it is frequently used in lieu of passivation and reportedly does a superior job.

Since you are going into a woods strike, my choice would be a 20 - 50% hydrochloric dip. Stronger is quicker, but corrodes everything around it. You might consider cathodic or periodic reverse current at a lower strength.

James Watts
- Navarre, Florida


No. 2 of 2 simultaneous responses:

(1998)

Dear Dave ,

Boy oh boy you have some problems , firstly the electro - polishing is producing a PASSIVE layer on the surface and must be removed before any plating is attempted , the whole purpose of electropolishing S/S is to obviously polish & deburr it but then to restore the oxide layer which gives the S/S its "Stainless" properties .

Secondly the very nature of the barrel plating process itself will produce more rejects plating S/S than conventional steel .

Activating S/S can be achieved in a bath of 10% HCl ( hydrochloric Acid )which has a means of reversing the current , start anodically & finish cathodically using about 10 Volts .

However whatever you try will give high reject rates just because of the barrel process , better results will be achieved with Racking the parts if possible

regards

John Tenison-Woods
John Tenison - Woods
- Victoria Australia


(1998)

I agree with John that barrel SS is more complicated to activate than rack parts. In order to plate in barrel , you need to activate it in the strike for a longer time (about three times as ling as for rack).

There are a lot of formulations for nickel strike solutions and it probably depends on the SS itself. My recommended formula is : 120 g/l Nickel chloride plus 10% v/v hydrochloride acid.

sara michaeli
sara michaeli signature 
Sara Michaeli
chemical process supplier
Tel-Aviv, Israel



(1998)

Another thing to look at is the EXACT type of SS. Customers had a horrible tendancy to tell me that it was 304 SS, neglecting to tell us that it was a free cutting one, and exactly which one. The additive to the alloy can make it very difficult to activate and may require a special activating acid.

Even tho you are buying certified material, from the same lot number, sometimes it is not. A sad fact of life. In critical operations it can make a significant difference.

James Watts
- Navarre, Florida



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView CURRENT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.