  Thread 198/24

Ford Spec. #ESB-M1P17-A

none
adv.
this text gets replaced with bannerText
spacer gets replaced with bannerImages

I would like to know the nickel plating thickness requirements for this specification.

John Welch
- Bronson, Michigan
2003
publicly reply to John Welch


2003

JOHN, PLATING THICKNESS FORD SPEC.ESB-M1P17-A. THIS IS THE SPEC FOR INTERIOR PART.

COPPER (d) 0.5 µm
NICKEL BRIGHT OR LOW GLOSS 7.6 µm
Total -not including 15.2 µm chrome
chromium significant 0.13 µm surface
Corrodkote, hrs 4 plating thickness measurement ( ASTM B487 )

Note : (d) Initial copper plate 0.5 µm in the strike may be replaced with nickel provided parts meet all other requirements of this specification.

popat patel
Popatbhai B. Patel
electroplating consultant - Roseville, Michigan
publicly reply to Popatbhai B. Patel



(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread


Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

Finishing
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g,
& Software


About/Contact  -  Privacy Policy  -  ©1995-2025 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"