Solderability Problem on Nickel Plated Headers


(2001)

I am doing a barrel tin plating and the materials to be plated is electroless nickel plated headers for ICs and transistors of metal cans (semiconductors). Currently; for the past 6 months until today I am facing this solderability problem.

The headers are electroless nickel plated and the caps are electrolytic nickel plated.

To eliminate the problem; the headers are treated with pure hydrogen at 400 deg celc; to reduce the oxidation.

How can you help me to resolve this problem? Kindly help.

Fazilah Hashim
semiconductors - Melaka, Malaysia



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView This Week's HOT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.