Current drops 30% from starting point in acid copper plating

November 16, 2011

Hallo,
Why after start of deposition of bright copper from acid bath, current density falls about by 30 pct?
Thanks

Gedas Bikulcius
student - Vilnius, Lithuania

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

Finishing
Jobshops Capital
Equipment Chemicals &
Consumables Consult'g,
& Software