Obtaining Thicker Chromic Anodize

A customer approached us with a challenge to consistently get 0.00016 inch minimum thickness on a Type I, chromic anodize job. Our standard 22 or 40 volt processes are unable to obtain this thickness. Does anyone out there have any suggestions for getting higher thicknesses?

Milton Stevenson
Plating Shop Owner - Syracuse, New York, USA
November 3, 2011

Sorry! Finishing.com is temporarily Read-Only.
Ted Mooney is retiring but I have several offers to take it over.
We're working hard to make sure we find it the best new home.

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: