What's the ruling if the Adhesion Test Sample snaps?





We are in the process of qualifying a vendor for electroless nickel plating to an internal specification similar to MIL-C-26074. If the adhesion test sample snaps before being bent 180 degrees, is it classed as a failure or does the inspection of loose particles at the fracture decide the success/failure?

The sample is AL6061-T6, .050 thick with .0009-.0015 nickel plating.

Cathy McEleney
Product Design - Cambridge, Massachusetts, USA
April 26, 2011




(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact  -  Privacy Policy  -  ©1995-2024 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"