Zinc thickness of different galvanization processes





September 9, 2010

What is coating thickness (in Microns) of Zinc in Pre Galvanized and Electrogalvanised Material after completing the Product? For Hot Dip Galvanized ,I believe the Thickness is min 55 Microns and Average is 80 Microns and For Corten A Materials the thickness would be 185 Microns Min. Am I right. Can you reply?

JIBIN PAUL
Sales Engineer - Doha ,Qatar



September 19, 2010

Sir
Hot Dip Galvanizing if you will follow british standard the thickness will vary from material to another such as if a big parts the thickness ( 80 to 120 microns) , for nails (40 to 45 microns), for sheets ( 15 till 35 microns)

Best Regards
Yasser Alshafee
Senior Chemist

Yasser Alshafee
steel factory - - Cairo, Egypt


none
finishing.com is made possible by ...
this text gets replaced with bannerText
spacer gets replaced with bannerImages

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact    -    Privacy Policy    -    ©1995-2023 finishing.com, Pine Beach, New Jersey, USA