Copper parts go black in 10-12 days after vibrofinishing



September 1, 2010

We get copper tubes or parts vibro finished and get shining finish.But after 10-12 days finish goes away leaving parts dull.How can we avoid it from happening.

RAVINDRANATHA MAROLI
Vibro finishing engineer - India



October 11, 2010

If you would like to avoid tarnishing of copper parts during storage, then you can use VPI coated papers/packs.

Formation of self-assembled monolayers of thiols is one way of preventing tarnishing of copper.

T.S.N. Sankara Narayanan
T.S.N. Sankara Narayanan
- Chennai, Tamilnadu, India
(ed.note Nov. 2017: The good doctor has a fascinating blog at https://advancementinscience.wordpress.com)

none
finishing.com is made possible by ...
this text gets replaced with bannerText
spacer gets replaced with bannerImages

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact    -    Privacy Policy    -    ©1995-2023 finishing.com, Pine Beach, New Jersey, USA