Preservation procedure for HRSG after hydrostatic test!





August 26, 2010

In couple of months, hydrostatic test of site assembled HRSG is to be conducted.
HRSG consists of following pressure parts viz Evaporator & Economiser. The material used for pressure parts is SA 106 Gr C & SA 106 Gr B. We want to know the correct preservation procedure after hydrostatic test for HRSG.

This HRSG is being erected in one of the steam plant in Oman where am employed as QC representative for owner company. Seek knowledge on the said subject.

Thank you for your time and sharing knowledge.

Regards

Raju Salvi
Employee - Oman


none
finishing.com is made possible by ...
this text gets replaced with bannerText
spacer gets replaced with bannerImages

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact    -    Privacy Policy    -    ©1995-2023 finishing.com, Pine Beach, New Jersey, USA