Maximum permissible lead in hot dip galvanizing?





August 16, 2010

I WANT TO KNOW THAT UP TO WHAT EXTENT PURITY OF LEAD IS RECOMMENDED TO USE IN HOT DIP GALVANIZING. IS PURITY OF 98.14% IS ACCEPTABLE. I SHALL BE VERY GRATEFUL FOR ANSWER AS EARLY AS POSSIBLE.

JAMEEL AKHTAR
PLANT INCHARGE - LAHORE,PAKISTAN



August 24, 2010

Sir:

It depends on what the impurities are and what are their percentages.

Regards,

Dr. Thomas H. Cook
Galvanizing Consultant - Hot Springs, South Dakota, USA


none
finishing.com is made possible by ...
this text gets replaced with bannerText
spacer gets replaced with bannerImages

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact    -    Privacy Policy    -    ©1995-2023 finishing.com, Pine Beach, New Jersey, USA