Corrosion resistance to dilute sulfuric acid




March 24, 2009

Dilute sulfuric acid at temperature? I have corrosion in some drums and pipes (100-110 C) containing hydroxylamine sulphate or hydroxylamine disulphonate
Is there any linings/coating that can be utilised under these conditions?
Is there any any stainless steel or high alloy steels can be utilised under these conditions?

Vicente Traver
Plant Inspector - Castellon, SPAIN



I've had a very good success with Halar* (ECTFE) coating working with H2So2

buena suerte !

Jordi Pujol
- Barcelona, Spain
May 14, 2009




(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

Finishing
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g,
& Software


About/Contact  -  Privacy Policy  -  ©1995-2024 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"