  Thread 502/06

Plating thickness checking in hot condition



I am working in a Brake lining manufacturing company.We have hard chrome plated compression moulds with a thickness of 25~30 microns. Moulds working temp is 150 °C. What is the facility and method available to check the plating thickness in this hot condition? I want to cary out to cross check the plating thickness online.

Kandasami Thiyagarajan
Mould management - Chennai,Tamil Nadu and India
October 6, 2008
publicly reply to Kandasami Thiyagarajan

There are magnetic devices. To my knowledge, they should work at that temperature w/o any problem. Maybe just a little re-calibration on a hot surface where the chrome thickness is known.

Guillermo Marrufo
Monterrey, NL, Mexico
October 9, 2008
publicly reply to Guillermo Marrufo



(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread


Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

Finishing
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g,
& Software


About/Contact  -  Privacy Policy  -  ©1995-2025 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"