Having problems hardcoating aluminum


(2000)

We are having problems hardcoating our aluminum. We can't get it to repeat.

My question is what is the best way to test the density of the acid tank and what should it read "avg".?

we are using a float hydrometer to test it now but have no idea what the reading should be. We are running it at 17 now. How to calibrate it for the temperature changes etc. I hope this makes sense. Any information on hardcoating aluminum will help

JOHN SMITH
- EAST CHINA MICH US


(2000)

Specific gravity can be used decently to control a chromic acid anodize tank but can not be used on a hardcoat line. First the density changes with temperature, so you would have to wait till the tank was cold to test it or develop a fudge factor. Second, Anodizing is concerned with the amount of sulfuric acid in the tank. You gradually build up aluminum and other contaminants that contribute to the specific gravity and give a false high reading. Switch to wet lab testing. It is accurate and does not take a lot of time (a lot more than a SG reading tho). You can also do a test for the amount of aluminum which you should be controlling also. This is not as easy a test to get repeatable data on, and rarely will two different people get the same answer on, but it is relative. Control the aluminum and your life will be better.

James Watts
- Navarre, Florida


(2000)

We might be able to help if you're willing to look at PVD approaches. To that end, What hard coating are you trying to apply, and what is the application?

jim treglio portrait
Jim Treglio
- Vista, California


(2000)

In this context 'hardcoating' has a specific meaning: it's a synonym for hardcoat anodizing, Jim.

Ted Mooney, finishing.com Teds signature
Ted Mooney, P.E. RET
finishing.com
Pine Beach, New Jersey



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView This Week's HOT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.