topic 4931

Nitriding and Shot Peening


(2000)

Recently, a failure of an H13 gas nitrided part was experienced. The failure apparently originated at the nitride white layer and propagated through the diffusion layer and base material.

  1. Has anyone experienced similar failures?
  2. Does anyone know of an easy way to remove the white layer formed during gas nitriding besides secondary machining?
  3. Finally, has anyone shot peened a nitrided surface with success? This last question addresses the question of possibly removing the white layer and introducing residual compressive stress to enhance fatigue properties.
Alan Simon
Dynisco HotRunners - Gloucester, MA USA


(2005)

I've just read that citric acid will remove the white layer. Or abrasive blasting. If the white is not removed From the surface it can cause fatigue problems in the future. I guess it did.

George Allen
- Harrisburg, Pennsylvania, USA



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView This Week's HOT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.