topic 4890

Magnesium in aluminum anodizing

(2000)

Good afternoon, My name is Ron Saladino I work for an anodizing co. in Pennsylvania. We have used what we call Mag bars in our process. They use Magnesium to attract stray electric to prevent pitting. We are in need of replacement bars. I am trying to find out what grade of magnesium is used for this application. I would appreciate any help you could give me. Thank you Ron Saladino

Ronald F. Saladino
- Readung, Pennsylvania



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Comment to THIS thread START a NEW threadView CURRENT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2018 finishing.com, Inc., Pine Beach, NJ   -   About finishing.com   -  Privacy Policy
How Google uses data when you visit this site.