topic 4444

Adhesion problem on Kovar


(2000)

Need help on this : I am plating electroless nickel on Kovar material, I use a 2% HF dip before a 50 degrees warm dip in 50% v/v HCl, however, I have adhesion problem and skip plating too.

any advice will be appreciated.

James lai
- singapore


(2000)

The only way I have found to be able to successfully plate on Kovar is to use a Watts nickel strike before the electroless.

John L Reid
- Brisbane, Qld, Australia



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView CURRENT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2018 finishing.com, Inc., Pine Beach, NJ   -   About finishing.com   -  Privacy Policy
How Google uses data when you visit this site.