Cathode selection when electropolishing 416 stainless steel




2006

When electropolishing 416 Stainless Steel what would be the best selection of a cathode? The goal obviously is to eliminate all free iron and sulfides from machining. Does the cathode selection matter? thanks

Franco Filice





(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact    -    Privacy Policy    -    ©1995-2023 finishing.com, Pine Beach, New Jersey, USA