Hard anodisation





I want to how hard anodisation increases the wear resistance? Can it be useful for mold material.If I use this as mold material then how much finish will I get in the sample prepared? What will be the longevity of the material? What type or grade of aluminium is required for hard anodisation? what will be the costing of hard anodisation? If possible I need the address of making my material hard anodised at Mumbai, India.

Sabyasachi Roy

2006

Ed. note: The site's supporting advertisers will contact you in private regarding your last sentence, Mr. Roy.

I think we can help you, because I'm already doing this in my aluminium moulds.

Pedro Oliveira

2006


adv. saify ind youtube



(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact  -  Privacy Policy  -  ©1995-2024 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"