Electropolishing for Nitinol wires
My name is Emanoel R. of Almeida, and I work in a parts factory for use orthodontics. I seek information on equipment and composition of the electrolyte for polishing of Nitinol (Ni-Ti alloys). Some attempts, in laboratory equipment, presented embrittlement, probably due to nascent hydrogen. Any information is of a lot of help. Thank you advance / Best Regards.
Emanoel Ribeiro de Almeida
SP - Brazil
Nitinol is subjected to hydrogen embrittlement. Bake after your process for 30 minutes @ 400 F. You will be ok again.Todd Huehn
- Blaine, Minnesota