Good day all,
Pang Cheng Lip
Designer - Singapore
I am developing a HS for electronics fully submerged in slow running saltwater.
the questions of corrosion resistance and thermal conductivity comes into play.
Some of the options available are:
salt resist / thermal conduction
monel/Inconel - good/poor
Titanium - good/poor
I am now looking at
1) Aluminium with electroless Ni-plating
2) Copper with electroless Ni-plating
No leaching allowed into the saltwater.
Appreciate all your insights and thoughts.
This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site
Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.
If you need a product/service, please check these Directories:
JobshopsCapital Equip. & Install'nChemicals & Consumables
Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices
How Google uses data when you visit this site.