topic 36246

ADC-10 Aluminum Alloy Environmental Properties


(2005)

I have some diecast boxes made from ADC-10 Aluminum Alloy and I wanted to know if they would tolerate 0 to 95% relative humidity without corrosion.

Edward Marden
aerospace systems - Hudson, New Hampshire


(2005)

Ed,
If you plan to anodize these boxes, they should withstand humidity. But does your querry include a salt spray test?

Michael Null
plater - Methuen, Massachusetts


January 21, 2010

ADC10 is an aluminum material used for die cast parts. What is an equivalent aluminum type to be used for sand casting?
Thank you

Marcello Tedesco
- Shelby Twp, Michigan



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView CURRENT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2018 finishing.com, Inc., Pine Beach, NJ   -   About finishing.com   -  Privacy Policy
How Google uses data when you visit this site.