What is Alonisation?


(1999)

I am looking information a treatment called ALONISATION. Does anybody know this treatment. I thank you in advance.

Laurent Schuster
- Belgium


(1999)

Alonizing is/was a process for applying a diffused coating of aluminum to ferrous materials to enhance corrosion/oxidation resistance. It has been many years since I have come across this process and I don't recall all of the details. I believe that parts to be coated were packed in a proprietary powder and heated to diffuse the aluminum into the steel or stainless steel substrate. Could this be the process that you are seeking?

larry hanke
Larry Hanke
materials testing laboratory
Minneapolis, Minnesota





This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView This Week's HOT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.