Sulfuric/oxalic anodizing


(1999)

For the shops anodizing using sulfuric/oxalic, what operating parameters (concentrations/temperature)do you run at? For a new bath makeup, what purity oxalic acid is required? Is technical grade sufficient, or would a more pure compound be advisable?

Thanks.

Pat Tierney

Patrick Tierney
Tobyhanna, Pennsylvania


(2001)

Please see the US patent No: 3046165. If you go into "Google.com" and search for "patent" you shall get the site of the US Patent office as the first entry. Best Luck and best regards.

Can APAK
- Istanbul, TURKEY



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView CURRENT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2018 finishing.com, Inc., Pine Beach, NJ   -   About finishing.com   -  Privacy Policy
How Google uses data when you visit this site.