Tantalum plating for pipe





2004

I have a high temp application (about 900C) that I would like to investigate the potential to use Tantalum plating. The application would be on pipe, internal & external, small diameter for hot gas applications. Does anyone actually do this?

Thanks,

Bill Mackay

William Mackay
metallizing & Coatings - Egg Harbor, New Jersey, USA

I would like to know what type of process is used to line pipe internals with tantalum material .

Hardeep Singh
- Klang, Selangor, Malaysia
2007




(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact  -  Privacy Policy  -  ©1995-2024 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"