ENP Vs HARD CHROME PLATING

FOR THE GIVEN APPLICATION OF potassium CARBONATE WUD LIKE TO KNOW THE COMPARISION OF SUITABILITY OF HARD CHROME PLATING Vs. ELECTROLESS NICKEL PLATING.

AMITABH ANAND
LARSEN & TOUBRO LIMITED - New Delhi, INDIA
2004

Too few givens, too many unknowns. ENP is more corrosion resistant than hard chrome in almost any environment, but generally less abrasion resistant, but that's about all that can be said.

Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey
Need quick confidential answers? $25
Need project assistance? $100/hr.
2004

Sorry! Finishing.com is temporarily Read-Only.
Ted Mooney is retiring but I have several offers to take it over.
We're working hard to make sure we find it the best new home.

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: