Crazing of hard anodize


(1999)

We have a customer that is concerned about the appearance of crazing on the surface of hard anodized (.0015" thk) 6063 extrusion. I have always felt this condition is typical on 6063, but I can not locate any written reference to the matter. Could anyone suggest where we might find a reference to this matter. Thanks, Herb Filbert

Herb Filbert
- Yorba Linda California



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView CURRENT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.