Pitting and Anodic corrosion in SS316 thin cylinders in marine environment




Dear Sir, We are facing Pitting Corrosion and Anodic Corrosion in SS316 cylinders with 6 mm and 8 mm wall thickness, which are deployed in sea for few months. Could you please suggest any cure. The nearest metal exposure to this component is Marine grade Aluminium 6061-T6. Though we are using sacrificing Zinc anodes we still face the same problem. hope to hear from you Gowtham

V.Gowtham
- Chennai, India
1999



2000

Dear Gowtham,

Please consider ANODIC PROTECTION instead of cathodic protection.

cheers

fadzli khir
- malaysia




(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact  -  Privacy Policy  -  ©1995-2024 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"