Peel off at the diecasted part after plating process


Currently we are receiving peel off complaint from our customer who assemble motor parts for the hard disk. The process goes, casting (ADC 12), shotblasting,then tumbling and plating. Before plating no peel found but after plating as high as 80% peeling is found.

Plating process done outside thru subcontractor at 85% Nitric acid and 15% hydrofluoric acid and cast part will be subjected to cleaning in caustic soda at 60°C before the etching process.

Consider this facts; 3(different models) items goes on the same processes from coating to the end process but only one item is severely affected.

I hope somebody can give us inputs.

Ramil Ranas
Aluminum Diecasting - Carmona, Cavite, Philippines

If you have a question in mind which seems off topic, please Search the Site

ADD a Q, A, or Comment on THIS topic START an UNRELATED topicView CURRENT HOT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices

©1995-2019, Inc., Pine Beach, NJ   -   About   -  Privacy Policy
How Google uses data when you visit this site.