Passivating Nitronic 60

2004

Does anyone have any experience passivating Nitronic 60? I am looking for the successes and the horror stories....Thanks

Robert Diffenderfer
plating company - Baltimore, Maryland

2004

Nitronic 60 will respond very well to non nitric acid passivation solutions. High manganese content makes it react slightly differently than 304 but will still give good results from passivation.

Dayton Dailey
- Lake Zurich, Illinois, USA

(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: