Long term effects of cadmium plated steel wire?


(1999)

We have a large amount of 1/32" dia. high carbon steel spring wire (carbon ~ 0.91%...ASTM A228) that has been cadmium plated per QQ-P-416 [link by ed. to spec at Defense Logistics Agency, dla.mil] , Type II, Class 2. This wire has been sitting in storage for over 20-years. What effect, if any, would the cadmium plating have on the steel over time? Should I notice a reduction in wire strength and/or fatigue? Theoretical as well as practical responses would be appreciated.

Marc Pepi
US Army - Aberdeen Proving Ground, Maryland


Coincidentally, I happened to have lunch yesterday with a retired chrome plating expert who related to me something that I had never heard of. It seems that when they used to do chrome plating of large heated rolls they discovered that there was no way to completely hydrogen relieve them. On the most difficult steam heated rolls, no matter what you did in terms of baking, even 2 weeks or more at 250-280 degrees F, if you plastic coated them the hydrogen would still come out an cause a bubble. Repair the bubble and it would reform. There was only one real cure for the problem: aging for a year before coating!

So I would surmise that after 20 years of aging, any concern for hydrogen embrittlement is over.

Ted Mooney, finishing.com Teds signature
Ted Mooney, P.E. RET
finishing.com
Pine Beach, New Jersey


(1999)

That does not mean that there was no damage. It would be a relatively simple to do some tensile strength testing on it and see if it is suitable for your purpose. I would also unroll a big part of the spool to see what corrosion might have take place down on the innards of the spool.

James Watts
- Navarre, Florida



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView This Week's HOT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.