Debonding problems with metallized PVC film


(1999)

I have some problems with debonding after metallizing PVC film for, for instance, sweets wrap. I would need some advise to improve the formulation based on tin carboxylate, GMO as internal lubricant and Loxiol G72 as external lubricant. Thank you sincerely for your help

Rafael Erro
- Barcelona, Spain


(2000)

Have you find any solution to your problem, we have been facing with the same difficulty.

Hoping to hear from you,

Neslig¸l Pervane
- Istanbul-Turkey


(2001)

Flame or spark treatment seems to be the only way to improve adhesion.

Rafael Erro
- Barcelona,Spain



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView CURRENT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.