pub  Where the
world gathers for metal finishing
Q&As since 1989



-----

Pin holes in 316SS heat exchanger in amine service




I found almost 1/3 plates of Plate Heat Exchanger (MOC- SS316) having pin holes. The PHE is being used in Amine service. can you suggest why pin holes are developed, rather amines are not such corrosive.

Damcrazy
engg - Mumbai, Maharashtra, India
2004



2004

Dear Mr Damcrazy,

This is a new name stranger than mine, thought I'd heard them all. The SS should have been passivated before use, even so I would have used titanium in the first place.

Khozem Vahaanwala
Khozem Vahaanwala
Saify Ind
supporting advertiser
Bengaluru, Karnataka, India
saify logo




(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact  -  Privacy Policy  -  ©1995-2024 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"