Black anodize on 380 die castings


(1999)

We are anodizing Type II Class 2 some gun parts that are 380 die castings. We know all of the problems associated with getting a good black color on a 380 die cast.

We are doing all we can, we give the pieces a rollbrite finish prior to anodize & we are using the Clariant black CRO dye which is supposed to work best on die castings.

Any one have any advice?

Should it be run at high voltage? Currently we are running at 15V.

Are we using the best Black dye for die castings?

We know we can use special pickles like nitric- hydrofluoric acid mix but we don't want to get involved with that on a production job.

Should it be run at a higher temp - currently running at 70 deg F for about 45 min or 75 deg F for 40 min.

Any advice greatly appreciated.

David A. Kraft
- Long Island City, New York



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView This Week's HOT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.