Nickel Plating/ Stress relief


(1999)

I'm currently restoring a 60's racing car and many parts will be nickel plated. In particular, a couple of suspension components and naturally I'm concerned about hydrogen embrittlement. Whilst the steel is not that hard (around 30-32 Rockwell) I'm keen to know what is required for proper stress relief of nickel plated parts.

Is there another method that gives the same "look" without the dangers of embrittlement?

Nick McDonald
- Australia


(1999)

Most people do not consider it necessary to bake after nickel plate on that low a Rc. If you feel that you want to bake, the standard is 375 F for 3 or 4 hours. Getting it into the bake cycle as soon as possible after plate is very helpful.

James Watts
- Navarre, Florida



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView CURRENT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.