Problem with stripping heavy copper plate after carburizing
Has anyone experienced the problem of stripping .0015" thick
(cyanide)copper plating after carburization and found small areas that seem resistant to stripping? We find, occasionally, that small areas of the copper plate start to strip, develop a black smut then stop stripping. The smut needs to be wiped off from these areas repeatedly after the majority of the plating has completely stripped.
Thanks in advance for any responses.
finishing shop - Minneapolis, Minnesota
This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site
Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.
If you need a product/service, please check these Directories:
JobshopsCapital Equip. & Install'nChemicals & Consumables
Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices
How Google uses data when you visit this site.