Stripping of Cu/Sn alloy





2003

I want to know how to strip a Copper/Tin alloy deposit. The deposit composition of Cu/Tin is 65/35. Thanks for your kindly help.

David Koo
- China



2003

Any question relating to stripping must include both the coating AND the base metal- otherwise the question is meaningless.

Geoffrey Whitelaw
Geoffrey Whitelaw
- Port Melbourne, Australia



2003

Thanks Geoff. The substrate is brass or zinc-die casting. And, the plating layer is copper and then Cu/Sn. Thanks for your help.

David Koo
- China


adv.:   
anoplex banner



(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact    -    Privacy Policy    -    ©1995-2023 finishing.com, Pine Beach, New Jersey, USA