Salt spray test





2003

For Cold Galvanizing Compound / Zinc Rich Paint, is there any method for getting accelerated salt spray corrosion. for testing 2000 hrs of salt spray corrosion .

Shail Mavani
LUBRICANTS - Mumbai, Maharashtra, India



2003

The short answer is no, Mr. Mavani. Accelerated corrosion testing is a quality control test, it is not a predictor of actual performance. But you could measure the thickness, which would be some indication of the real life performance.

Ted Mooney, finishing.com
Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey


none
finishing.com is made possible by ...
this text gets replaced with bannerText
spacer gets replaced with bannerImages



(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact    -    Privacy Policy    -    ©1995-2023 finishing.com, Pine Beach, New Jersey, USA