GEL FOR ACIDS




FOR CLEAN THE WELDINGS SIDES IN STAINLESS STEEL PARTS, IS NORMAL TO USE A ACID MIX HF + NO3H, BUT IS DANGEROUS. I READ THAT IS possible TO USE IN GEL FORM. CAN YOU HELP MI FOR TO FIND ANY PRODUCT FOR "GELIFICAR " THE MIXTURE OF THIS ACIDS?

REGARDS,

BRUN ANTONIO
- CASTELLDEFELS, BARCELONA, SPAIN
2003



For cleaning the weld areas of stainless steel parts, it is normal to use an acid mix of HF + HNO3, but it is dangerous. I read that is possible to use this in gel form. Can you help me find any product for "gelifying " the mixture of these acids?

Regards,

Kadir Levent
- Istanbul, Turkey
2004




(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact  -  Privacy Policy  -  ©1995-2024 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"